Integrated circuits with varying gate structures and fabrication methods

ABSTRACT

Integrated circuits and fabrication methods are provided. The integrated circuit includes: a varying gate structure disposed over a substrate structure, the varying gate structure including a first gate stack in a first region of the substrate structure, and a second gate stack in a second region of the substrate structure; a first field-effect transistor in the first region, the first field-effect transistor including the first gate stack and having a first threshold voltage; and a second field-effect transistor in the second region, the second field-effect transistor including the second gate stack and having a second threshold voltage, where the first threshold voltage is different from the second threshold voltage. The methods include providing the varying gate structure, the providing including: sizing layer(s) of the varying gate structure with different thickness(es) in different region(s).

FIELD OF THE INVENTION

The present invention relates to semiconductor devices and methods ofmanufacturing semiconductor devices, and more particularly, tointegrated circuits and methods for fabricating integrated circuits withvarying gate structures.

BACKGROUND OF THE INVENTION

Different semiconductor devices may be fabricated to have one or moredifferent device characteristics, such as threshold voltage, switchingspeed, leakage power consumption, etc. Multiple different designs mayeach provide optimization of one or more of these characteristics fordevices intended to perform specific functions. For instance, one designmay have reduced threshold voltage to increase switching speed fordevices providing computational logic functions, and another design mayhave increased threshold voltage to decrease power consumption fordevices providing memory storage functions. A system using multiplediscrete devices, each optimized for different functions, will result ingreater system complexity, increased system footprint, and added systemcost.

BRIEF SUMMARY

The shortcomings of the prior art are overcome, and additionaladvantages are provided, through the provision, in one aspect, of anintegrated circuit. The integrated circuit includes a varying gatestructure disposed over a substrate structure, the varying gatestructure having a first gate stack in a first region of the substratestructure, and a second gate stack in a second region of the substratestructure; a first field-effect transistor in the first region of thesubstrate structure, the first field-effect transistor including thefirst gate stack of the varying gate structure and having a firstthreshold voltage; and a second field-effect transistor in the secondregion of the substrate structure, the second field-effect transistorincluding the second gate stack of the varying gate structure and havinga second threshold voltage, where the first threshold voltage isdifferent from the second threshold voltage.

In another aspect, a method for fabricating an integrated circuit ispresented herein. The method includes providing a varying gate structuredisposed over a substrate structure, the varying gate structure having afirst gate stack in a first region of the substrate structure and asecond gate stack in a second region of the substrate structure, and theproviding including: sizing one layer of the varying gate structure witha first thickness in the first region of the substrate structure and asecond thickness in the second region of the substrate structure; andsizing another layer of the varying gate structure with a thirdthickness in the first region of the substrate structure and a fourththickness in the second region of the substrate structure, where thefirst thickness is different from the second thickness, and the thirdthickness is different from the fourth thickness.

Additional features and advantages are realized through the techniquesof the present invention. Other embodiments and aspects of the inventionare described in detail herein and are considered a part of the claimedinvention.

BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS

One or more aspects of the present invention are particularly pointedout and distinctly claimed as examples in the claims at the conclusionof the specification. The foregoing and other objects, features, andadvantages of the invention are apparent from the following detaileddescription taken in conjunction with the accompanying drawings inwhich:

FIG. 1A is a plan view of one embodiment of an intermediate circuitstructure obtained during circuit fabrication, and depicts a varyinggate structure disposed over a substrate structure, in accordance withone or more aspects of the present invention;

FIG. 1B is an isometric view of one embodiment of an integrated circuit,in accordance with one or more aspects of the present invention;

FIGS. 2A-2B are cross-sectional elevation views of the structure of FIG.1A, and depict the varying gate structure having first and second gatestacks, in accordance with one or more aspects of the present invention;

FIG. 3 illustrates the structure of FIGS. 2A-2B after providing aprotective mask over a first region of the substrate structure, inaccordance with one or more aspects of the present invention;

FIGS. 4A-4B depict the structure of FIG. 3 after removing, at leastpartially, material from a second region of the substrate structure, inaccordance with one or more aspects of the present invention;

FIGS. 5A-5B depict the structure of FIGS. 4A-4B after sizing one layerof the varying gate structure, in accordance with one or more aspects ofthe present invention;

FIGS. 6A-6B depict the structure of FIGS. 5A-5B after depositing, atleast partially, another material of another layer over the substratestructure, in accordance with one or more aspects of the presentinvention;

FIG. 7 illustrates the structure of FIGS. 6A-6B after providing aprotective mask over the second region of the substrate structure, inaccordance with one or more aspects of the present invention;

FIGS. 8A-8B depict the structure of FIG. 7 after removing, at leastpartially, the other material from the first region of the substratestructure, in accordance with one or more aspects of the presentinvention;

FIGS. 9A-9B depict the structure of FIGS. 8A-8B after sizing the otherlayer of the varying gate structure, in accordance with one or moreaspects of the present invention;

FIG. 10 illustrates the structure of FIGS. 9A-B after providing aprotective mask over a third region of the substrate structure, inaccordance with one or more aspects of the present invention;

FIG. 11A depicts the structure of FIG. 10 after chamfering the otherlayer of the varying gate structure in a fourth region of the substratestructure, in accordance with one or more aspects of the presentinvention;

FIG. 11B depicts the structure of FIG. 10 after sizing the other layerof the varying gate structure in the third region of the substratestructure, in accordance with one or more aspects of the presentinvention;

FIGS. 12A-12B depict the structure of FIGS. 11A-11B after providinganother layer over the substrate structure, in accordance with one ormore aspects of the present invention; and

FIG. 13A-13B depict the structure of FIGS. 12A-12B after filling thevarying gate structure with another material, in accordance with one ormore aspects of the present invention.

DETAILED DESCRIPTION

Aspects of the present invention and certain features, advantages, anddetails thereof, are explained more fully below with reference to thenon-limiting examples illustrated in the accompanying drawings.Descriptions of well-known materials, fabrication tools, processingtechniques, etc., are omitted so as not to unnecessarily obscure theinvention in detail. It should be understood, however, that the detaileddescription and the specific examples, while indicating aspects of theinvention, are given by way of illustration only, and not by way oflimitation. Various substitutions, modifications, additions, and/orarrangements, within the spirit and/or scope of the underlying inventiveconcepts will be apparent to those skilled in the art from thisdisclosure.

The present disclosure provides, in part, integrated circuits, includingfield-effect transistors (FETs), having a varying gate structure andmultiple different threshold voltages. During integrated circuitfabrication, numerous gates for numerous FETs may be desired in a singleprocess which provides one or more gate structures above selectedregions of an entire substrate of the integrated circuit. For instance,a layered gate structure, having a uniform stack of layers of materials,may be provided above the selected regions of the entire substrate toform numerous gates for numerous FETs. As used herein, a varying gatestructure refers to a gate structure that has multiple different stacksof layers, or multiple different gate stacks, that may have differentcompositions or sizes, in different regions of the integrated circuit.In one example, such a varying gate structure may have differentmaterial layers of different thicknesses in the same or differentregions. In another example, such a varying gate structure may have adifferent number of material layers in different regions. By using avarying gate structure as described herein, numerous gates withdifferent gate stacks may be formed in a single process.

In a FET, the threshold voltage is the minimum gate voltage required toallow current to flow from a source to a drain through a channel of theFET. Controlling for other factors, in general, a FET with a lowerthreshold voltage operates faster, but consumes more leakage power, thana FET with higher threshold voltage.

When designing integrated circuits, including, for example, systems on achip, for use in specific applications, such as mobile phones or mediaplayers, it may be desirable to optimize leakage power consumption andspeed of the integrated circuit by having different portions of theintegrated circuit implemented with FETs having different thresholdvoltages. For example, it may be desirable to perform logic orarithmetic functions at a relatively higher speed to enable advancedfeatures, and to perform memory storage at a relatively lower speed tosave power. In another example, even within a single logic subsystem ofan integrated circuit, it may be desirable to optimize the speed ofcertain FETs and optimize the power consumption of other FETs.

In addition, because modern integrated circuit designs rely oncomplementary metal oxide semiconductor (CMOS) technology, using bothn-type FETs (NFETs) and p-type FETs (PFETs), integrated circuitscombining NFETs and PFETs with multiple threshold voltages aredesirable.

Generally stated, provided herein, in one aspect, is an integratedcircuit. The integrated circuit includes a varying gate structuredisposed over a substrate structure, the varying gate structure having afirst gate stack in a first region of the substrate structure, and asecond gate stack in a second region of the substrate structure; a firstfield-effect transistor in the first region of the substrate structure,the first field-effect transistor including the first gate stack of thevarying gate structure and having a first threshold voltage; and asecond field-effect transistor in the second region of the substratestructure, the second field-effect transistor including the second gatestack of the varying gate structure and having a second thresholdvoltage, where the first threshold voltage is different from the secondthreshold voltage. In one example, a portion of the varying gatestructure extends from the first field-effect transistor to the secondfield-effect transistor. In another example, the first threshold voltagemay be between 80 and 120 millivolts greater than the second thresholdvoltage. In a further example, the one layer of the varying gatestructure comprises a work-function layer, and the other layer of thevarying gate structure comprises a cap layer, and the varying gatestructure further comprises a gate dielectric layer disposed below thecap layer.

In one embodiment, the varying gate structure may include one layer andanother layer, the one layer having a first thickness in the firstregion of the substrate structure and a second thickness in the secondregion of the substrate structure, and the other layer having a thirdthickness in the first region of the substrate structure and a fourththickness in the second region of the substrate structure, where thefirst thickness is different from the second thickness, and the thirdthickness is different from the fourth thickness. In such a case, thefirst thickness is less than the second thickness, and the thirdthickness is greater than the fourth thickness.

In another embodiment, the substrate structure may include a first finextending over the first region of the substrate structure and a secondfin extending over the second region of the substrate structure, and thevarying gate structure may be conformally disposed over the first finand the second fin. In such a case, the first fin and the second fin maybe a common fin.

A method for fabricating an integrated circuit is also provided herein.The method includes providing a varying gate structure disposed over asubstrate structure, the varying gate structure having a first gatestack in a first region of the substrate structure and a second gatestack in a second region of the substrate structure, and the providingincluding: sizing one layer of the varying gate structure with a firstthickness in the first region of the substrate structure and a secondthickness in the second region of the substrate structure; and sizinganother layer of the varying gate structure with a third thickness inthe first region of the substrate structure and a fourth thickness inthe second region of the substrate structure, where the first thicknessis different from the second thickness, and the third thickness isdifferent from the fourth thickness.

In one example, the integrated circuit includes a first field-effecttransistor in the first region of the substrate structure, and a secondfield-effect transistor in the second region of the substrate structure,the first field-effect transistor including the first gate stack andhaving a first threshold voltage, and the second field-effect transistorincluding the second gate stack and having a second threshold voltage,where the first threshold voltage is different from the second thresholdvoltage. In another example, a third region of the substrate structureincludes a portion of the first region and another portion of the secondregion, and the providing further includes, after sizing the one layerof the varying gate structure, resizing the one layer in the thirdregion of the substrate structure with a fifth thickness.

In one embodiment, sizing the one layer of the varying gate structuremay include: depositing, at least partially, a material of the one layerover the first region and the second region of the substrate structure;removing, at least partially, the material from the first region of thesubstrate structure; and depositing again, at least partially, thematerial over the first region and the second region of the substratestructure to form the first thickness of the one layer in the firstregion, and the second thickness of the one layer in the second region.

In another embodiment, the substrate structure includes one or more finsextending over the first region and the second region thereof, andproviding the varying gate structure includes providing the varying gatestructure conformally over the one or more fins. In such a case, theintegrated circuit may include a first field-effect transistor in thefirst region of the substrate structure and a second field-effecttransistor in the second region of the substrate structure, the firstfield-effect transistor including the first gate stack and a first finof the one or more fins, and having a first threshold voltage, and thesecond field-effect transistor including the second gate stack and asecond fin of the one or more fins, and having a second thresholdvoltage, where the first threshold voltage is different from the secondthreshold voltage.

Reference is made below to the drawings, which are not drawn to scalefor ease of understanding, wherein the same reference numbers usedthroughout different figures designate the same or similar components.

FIG. 1A illustrates one embodiment of an intermediate circuit structure100 obtained during circuit fabrication, in accordance with one or moreaspects of the present invention. In one example, as depicted, a gatestructure 120 is disposed over a substrate structure. As depicted, inone example, the substrate structure may include a substrate 102 and oneor more fins 110, supporting the formation of fin-type field-effecttransistors (Fin FETs) and planar FETs.

Gate structure 120 may extend conformally over (and partially wraparound) the one or more fins 110. In one example, a replacement gateprocess may be employed, wherein a sacrificial gate of an appropriatematerial, such as polycrystalline silicon (polysilicon), may be providedat an early stage of circuit fabrication, and then later removed andreplaced with a final gate structure. In another example, the gatestructure may be formed directly without the use of a sacrificial gate.In either gate process, the gate structure may be formed either before(gate-first) or after (gate-last) the formation of a source region and adrain region of field effect transistors, depending upon the processflow selected.

Substrate 102 may be (in one example) a bulk semiconductor material suchas a bulk silicon wafer. As another example, substrate 102 may be orinclude any silicon-containing substrate including, but not limited to,single crystal Si, polycrystalline Si, amorphous Si, Si-on-nothing(SON), Si-on-insulator (SOI), or Si-on-replacement insulator (SRI)substrates and the like, and may be n-type or p-type doped as desiredfor a particular application. In one example, substrate 102 may be, forinstance, a wafer or substrate approximately 600-700 micrometers thick,or less.

Fins 110 may extend from substrate 102, and may include one or more finsin first region 131 and one or more fins in second region 132. By way ofexample, fins may be formed by removing one or more portions of thesubstrate to create the fins from the same material as the substrate,such as, for example, a semiconductor or crystalline material. In oneexample, formation of fins may be achieved by patterning the substrateusing any of various approaches, including: direct lithography; sidewallimage transfer technique; extreme ultraviolet lithography (EUV); e-beamtechnique; litho-etch litho-etch; or litho-etch litho-freeze. Followingpatterning, material removal may be performed, for example, by anysuitable etching process, such as an anisotropic dry etching process,for instance, reactive-ion-etching (RIE) in sulfur hexafluoride (SF₆).Although the following numbers are relative and the heights could vary,as one specific example, fins may have a height of about 40 nanometers,and a length of about one micrometer, several micrometers, or thediameter of the entire wafer, and the thickness of fins may beapproximately 10 nanometers or less. In another example, the fins may beformed on the substrate, and the fins and the substrate may be differentmaterials.

Referring to FIG. 1B, one embodiment of an integrated circuit 100′having two field-effect transistors (FETs) is illustrated to provideoverall context regarding the present invention. As shown, a portion ofgate structure 120′ may extend from a first FET in region 133 to asecond FET in region 134, and each FET may include two fins 110. In atypical integrated circuit, thousands, millions, or more, FETs may beinterconnected. In complementary metal-oxide-semiconductor (CMOS)technology, n-type FETs (NFETs) may be interconnected with p-type FETs(PFETs), for example, by sharing a common gate structure, or may beconnected by metal contacts (not shown). Each FET may include, forinstance, any number of fins, depending on the desired circuit design,because having more fins may allow the FET to carry a greater currentfrom a source 112 to a drain 114. For example, as depicted each FET hastwo fins. In a given integrated circuit, there may be a variety of FETshaving varying numbers of fins interspersed throughout the integratedcircuit.

For reasons explained above, it may be desirable for different FETs ofan integrated circuit to have different threshold voltages. As disclosedherein, a varying gate structure having different gate stacks indifferent regions may allow for different threshold voltages to beselected for FETs in those different regions. In addition, because ofthe different electrical characteristics of NFETs and PFETs, the varyinggate structure may allow for the same or similar threshold voltages tobe selected for NFETs and PFETs, including NFETs and PFETs directlyconnected by a portion of the varying gate structure. In some cases,there may be a requirement for six or more different threshold voltages.For example, a CMOS integrated circuit may require a pair of regularthreshold voltages, a pair of low threshold voltages, and a pair ofsuper-low threshold voltages, with each pair providing a thresholdvoltage for each of NFETs and PFETs.

Gate structure 120′ may be formed, for example, using the techniquesdisclosed herein, and may have one gate stack in region 133 and adifferent gate stack in region 134, allowing for different thresholdvoltages to be selected for FETs in those different regions. In anotherexample, a varying gate structure that has different gate stacks inregion 133 and region 134 may allow for the same (or a similar)threshold voltage to be selected for an NFET in region 133 and a PFET inregion 134.

FIG. 2A illustrates the structure of FIG. 1A, taken along line 2A-2Athereof, and varying gate structure 120 extending over fin 110. Asshown, in this example, gate structure 120 is in an intermediate stageof fabrication. Spacers 112 may facilitate formation of multiple layersby, for example, containing the material deposited to form each layer.In one example, a gate structure could include a dielectric layer 122, acap layer 124, and another cap layer 126. Also note that an interfaciallayer 121 may be provided between the substrate and dielectric layer122.

By using a series of protective masks that protect some regions of thesubstrate structure and expose regions of the substrate structure, avarying gate structure, rather than a uniform gate structure, may beformed, with multiple different gate stacks, such as material layershaving varying thicknesses, in multiple different regions, enabling FETshaving multiple different threshold voltages. The varying gate structuremay enable multiple different threshold voltages because the thresholdvoltage of a FET is influenced by the electrical properties of the gate,which is located between a channel of the FET and a gate contact thatapplies a gate voltage to the gate. By sizing or tuning the varying gatestructure to have different gate stacks in different regions, differentthreshold voltages may be achieved, because in a FET, the thresholdvoltage is directly related to how the gate voltage influences thebehavior of charge carriers located in a channel underlying the gate.

In one example, dielectric layer 122 may be a material includingsilicon, such as silicon dioxide, or silicon oxynitride. In anotherexample, dielectric layer 122 may be a high dielectric constant (high-k)material having a dielectric constant greater than, for example,approximately 3.9 (the dielectric constant of silicon dioxide),including, but not limited to one or more of hafnium oxide, tantalumoxide, zirconium oxide, titanium oxide, or aluminum oxide. In onespecific example, dielectric layer 122 may be a high-k material having athickness of approximately 15 angstroms (Å). Interfacial layer 121 mayfacilitate formation of dielectric layer 122, and may be, for example, achemical oxide of the underlying substrate, such as silicon dioxide,having a thickness of approximately 9 Å.

Cap layer 124 may be included to protect dielectric layer 122 fromdamage during various processing steps. In one example, cap layer 124may be or include titanium nitride (TiN) or tantalum nitride (TaN), andmay have a thickness of approximately between 10 Å and 15 Å, and in onespecific example, may be a TiN layer with a thickness of 12 Å.

Each of dielectric layer 122, cap layer 124, and cap layer 126, may bedeposited using any of a variety of deposition processes, including, forexample, physical vapor deposition (PVD), atomic layer deposition (ALD),chemical vapor deposition (CVD), sputtering, or other processes,depending on the material composition of the layer. The deposition mayconform to the substrate structure, including wrapping around fins 110.

FIG. 2B illustrates the structure of FIG. 1, taken along line 2B-2Bthereof. In one embodiment of the fabrication methods disclosed herein,at the stage of fabrication illustrated in FIGS. 2A-2B, gate structure120 may include similar layers having similar sizes in first region 131and second region 132. In another example, the sizes and composition ofthe layers may already vary at the stage of fabrication depicted.

FIGS. 3-5B illustrates one embodiment of a process for sizing a layer ofgate structure 120. In this set of examples, a cap layer of gatestructure 120 may be sized to have different thicknesses in differentregions of the substrate structure. Typically, a cap layer may be usedto protect an underlying dielectric layer, and is not ordinarily viewedas influencing the threshold voltage. However, as disclosed herein,varying the size of the cap layer may shift the position of other layersof the varying gate structure, thereby changing the electricalproperties thereof. Such a shift in the layers, and change in theelectrical properties, can lead to different threshold voltages.

In the process depicted in FIGS. 3-5B, an additive and subtractiveprocess is used to size a cap layer. Such a process may be preferable toan additive only process, because deposition processes used to addmaterial to the cap layer may not be compatible with masking techniquesrequired. However, if appropriate masking techniques may be used, thenan additive only process could be used to size the cap layer.

FIG. 3 illustrates the structure of FIGS. 2A-2B after providing aprotective mask 141 over first region 131 of the substrate structure,leaving second region 132 exposed to the further processing steps to bedisclosed with respect to FIGS. 4A-4B. A protective mask 141 may beprovided over the entire circuit structure 100, and then patterned usingstandard lithographic processing, to reveal second region 132, andprotect first region 131. FIG. 3 illustrates one portion of a largerintegrated circuit, and first region 131 may be a discontinuous regionhaving many portions protected by protective mask 141, depending uponthe specific integrated circuit being fabricated.

In one example, protective mask 141 may include a material such as, forexample, silicon nitride, silicon oxide, or silicon oxynitride, and maybe deposited using conventional deposition processes, such as, forexample, CVD or plasma-enhanced CVD (PECVD). In other examples, othermask materials may be used depending upon the materials used in circuitstructure 100. For instance, protective mask 141 may be or include anorganic material. For instance, flowable oxide such as, for example, ahydrogen silsesquioxane polymer, or a carbon-free silsesquioxanepolymer, may be deposited by flowable chemical vapor deposition (F-CVD).In another example, protective mask 141 may be or include an organicpolymer, for example, polyacrylate resin, epoxy resin, phenol resin,polyamide resin, polyimide resin, unsaturated polyester resin,polyphenylene ether resin, polyphenylenesulfide resin orbenzocyclobutene (BCB).

FIG. 4A illustrates the structure of FIG. 3, taken along line 4A-4Athereof, and FIG. 4B illustrates the structure of FIG. 3, taken alongline 4B-4B thereof. As depicted, in one example, a process for sizingcap layer 126 includes removing material of cap layer 126 from secondregion 132 of the substrate structure, and leaving unchanged cap layer126 in first region 131. In another example, the material may be removedpartially, in order to reduce a thickness of cap layer 126 in secondregion 132.

Removing cap layer 126 may be achieved by any suitable etching process,such as dry or wet etching processing. In one example, isotropic dryetching may be used by, for example, ion beam etching, plasma etching orisotropic RIE. In another example, isotropic wet etching may also beperformed using etching solutions selective to the material of cap layer126. Protective mask 141 ensures that material of cap layer 126 is notremoved from first region 131 during such a removal process.

FIGS. 5A-5B illustrate the structure of FIGS. 4A-4B after removing theprotective mask and depositing material of cap layer 126 over firstregion 131 and second region 132 of the substrate structure. In oneexample, as depicted, depositing the material provides cap layer 126with a first thickness T₁ in first region 131, and a second thickness T₂in second region 132. As depicted T₁ may be greater than T₂, but inanother example, T₂ may be greater than T₁. The material may bedeposited by variety of deposition processes, including, for example,physical vapor deposition (PVD), atomic layer deposition (ALD), orchemical vapor deposition (CVD). For example, cap layer 126 may be orinclude TiN or TaN, and have a thickness between 10 Å and 18 Å. In onespecific example, cap layer 126 may be TaN, and have thickness T₁ ofbetween 15 Å and 18 Å in first region 131, and thickness T₂ of 10 Å insecond region 132.

Removing the protective mask may be achieved using any suitable process,such as chemical-mechanical polishing (CMP), or etching, depending onthe chemistry of the protective mask.

FIGS. 6A-9B illustrate examples of a process of sizing (or varying)another layer of gate structure 120. In these examples, a work-functionlayer of varying gate structure 120 may be sized to have differentthicknesses in different regions of the substrate structure, enablingdifferent gate stacks in the different regions. For a conductor, thework-function is an electrical property that describes the minimumenergy required to remove an electron from the conductor. Awork-function layer of a gate structure, therefore, is a material layerthat directly impacts the threshold voltage because it influences theamount of energy required for electrons to flow from the gate stack to agate contact, and thereby influences the amount of energy available toattract charge carriers in a channel underlying the gate. In addition,the previously described process of sizing a cap layer may influence thevertical position of the after formed work-function layer with respectto the underlying channel. These different factors work together toallow the creation of a varying gate structure defining differentthreshold voltages.

FIGS. 6A-6B illustrate the structure of FIGS. 5A-5B after depositing amaterial of a work-function layer 128 over first region 131 and secondregion 132. The material of work-function layer 128 may be formed usingany of the deposition processes described for depositing cap layer 126,with respect to FIGS. 5A-5B.

Work-function layer 128 may be or include metals and their nitrides,such as titanium nitride (TiN), tantalum nitride (TaN), titaniumaluminum nitride (TiAlN), tantalum aluminum nitride (TaAlN), niobiumnitride (NbN), vanadium nitride (VN), tungsten nitride (WN). In anotherexample, work-function layer 128 may be or include metals and theircarbides, such as titanium carbide (TiC), titanium aluminum carbide(TiAlC), titanium aluminide (TiAl) tantalum carbide (TaC), tantalumaluminum carbide (TaAlC), niobium carbide (NbC), vanadium carbide (VC),etc. In another example, work-function layer 128 may also includeruthenium (Ru), platinum (Pt), molybdenum (Mo), cobalt (Co) and alloysand combinations thereof.

FIG. 7 illustrates the structure of FIGS. 6A-6B after providing anotherprotective mask 142 over second region 131 of the substrate structure,leaving first region 131 exposed to the further processing steps to bedisclosed with respect to FIGS. 8A-8B. Protective mask 142 may have anyof the properties previously described with respect to the protectivemask of FIG. 3.

FIG. 8A illustrates the structure of FIG. 7, taken along line 8A-8Athereof, and FIG. 8B illustrates the structure of FIG. 7, taken alongline 8B-8B thereof. As depicted, in one example, a process for sizingwork-function layer 128 includes removing material of work-functionlayer 128 from first region 132 of the substrate structure. In anotherexample, the material may be removed partially, in order to reduce athickness of work-function layer 128 in first region 131. Removingwork-functional layer 128 may be achieved using any of the removalprocesses described for removing cap layer 126 with respect to FIGS.4A-4B.

FIGS. 9A-9B illustrate the structure of FIGS. 8A-8B after removing theother protective mask and depositing the material of work-function layer128 over first region 131 and second region 132. In one example, asdepicted, depositing the material forms a first thickness T′₁ ofwork-function layer 128 in first region 131, and a second thickness T′₂in second region 132. As depicted T′₂ may be greater than T′₁, but inanother example, T′₁ may be greater than T′₂. Depositing material ofwork-function layer 128 may be accomplished using the techniquespreviously described with respect to FIGS. 6A-6B.

For example, work-function layer 128 may be or include TiN or TiC andmay have a thickness of approximately between 20 Å and 60 Å. In onespecific example, work-function layer 128 may be a TiN layer withthickness T′₂ in second region 132 of approximately 20 Å, and thicknessof T′₁ in first region of approximately 40 Å. In such an example, alongwith sized cap layer 126, the first gate stack may define a firstthreshold voltage for a FET in first region 131 of approximately 0.35 Vand a second threshold voltage for another FET in second region 132 ofapproximately 0.25 V, that are different by between 80 and 120milivolts.

FIG. 10 illustrates the structure of FIGS. 9A-9B after providing anotherprotective mask 143 over a third region 133 of the substrate structure,leaving a fourth region 134 of the substrate structure exposed to thefurther processing steps to be disclosed with respect to FIG. 11A. Asillustrated, third region 133 and fourth region 134 each overlap firstregion 131 and second region 132. In one example, varying gate structure120 may have one gate stack in third region 133 to provide a thresholdvoltage for PFETs, and another gate stack in fourth region 134 toprovide a different threshold voltage for NFETs. By using protectivemasks and overlapping regions, varying gate structure 120 can havedifferent layers of different thickness in numerous regions, allowingfor any number of threshold voltages to be defined, as required by thecircuit design.

FIG. 11A illustrates the structure of FIG. 10 after chamferingwork-function layer 128 in the fourth region of the substrate structure.Work-function layer 128 may optionally be chamfered to remove sharpcorners, in order to facilitate subsequent processing steps, becausenarrow openings of gate structure 120 may make it difficult to depositfurther materials. Chamfering may be achieved by any appropriate etchingprocess, such as isotropic etching.

FIG. 11B illustrates the structure of FIG. 10 after removing thework-function layer in the third region of the substrate structure. Toremove the work-function layer, a protective mask may be provided overthe fourth region of the substrate structure and a removal process maybe employed in a like manner as previously described with respect toFIGS. 7-8B. In another example, only a portion of the work-functionlayer may be removed.

FIGS. 12A-12B illustrate the structure of FIGS. 11A-11B after providinganother layer 129 over the substrate structure. In one example, otherlayer 129 may be a work-function layer, and may be the same or adifferent material as work-function layer 128. Using the techniquespreviously described, other layer 129 may be sized with differentthicknesses in different regions of the substrate structure.

FIGS. 13A-13B illustrate the structure of FIGS. 12A-12B after depositingan encapsulation layer 130′ and filling varying gate structure 120 witha material 130. In one example, material 130 may be any suitablematerial, including a metal, such as tungsten (W). Encapsulation layer130′ may be needed to protect the underlying gate stack from mechanicaldamage or diffusion of material 130, and may be, in one specificexample, TiN having a thickness of 20 Å. Because of the varying totalheight of varying gate structure 120, a sufficient amount of material130 may be deposited to completely fill gate structure 120. Afterfilling the gate structure 120 with material 130, the circuit structuremay be subjected to a chemical mechanical polishing (CMP) process toremove extra gate stack material from various portions of the circuitstructure.

As illustrated, varying gate structure 120 may have different layers ofmaterials, including work-function and cap layers, having differentsizes in various regions of the substrate structure. Taken together,FIGS. 13A-13B illustrate four different gate stacks of varying gatestructure 120 having four different size profiles, allowing for fourdifferent threshold voltages. As may be readily understood, by applyingthe techniques disclosed herein, varying gate structure 120 may be tunedin additional regions to yield additional different gate stacks, andtherefore, different threshold voltages, including for exampleadditional different pairs of threshold voltages for NFETs and PFETs.

In addition, under certain circumstances, it may be desirable to furthertune the threshold voltages achieved using the varying gate structuredescribed herein, by implanting impurities, such as n-type or p-typedopants, within portions of the circuit structure, such as a channelregion underlying the gate structure, or the various layers described.Such tuning may be achieved by plasma doping or ion implantation of thecircuit structure using various materials.

The terminology used herein is for the purpose of describing particularembodiments only and is not intended to be limiting of the invention. Asused herein, the singular forms “a,” “an,” and “the” are intended toinclude the plural forms as well, unless the context clearly indicatesotherwise. It will be further understood that the terms “comprise” (andany form of comprise, such as “comprises” and “comprising”), “have” (andany form of have, such as “has” and “having”), “include” (and any formof include, such as “includes” and “including”), and “contain” (and anyform contain, such as “contains” and “containing”) are open-endedlinking verbs. As a result, a method or device that “comprises,” “has,”“includes,” or “contains” one or more steps or elements possesses thoseone or more steps or elements, but is not limited to possessing onlythose one or more steps or elements. Likewise, a step of a method or anelement of a device that “comprises,” “has,” “includes,” or “contains”one or more features possesses those one or more features, but is notlimited to possessing only those one or more features. Furthermore, adevice or structure that is configured in a certain way is configured inat least that way, but may also be configured in ways that are notlisted.

The corresponding structures, materials, acts, and equivalents of allmeans or step plus function elements in the claims below, if any, areintended to include any structure, material, or act for performing thefunction in combination with other claimed elements as specificallyclaimed. The description of the present invention has been presented forpurposes of illustration and description, but is not intended to beexhaustive or limited to the invention in the form disclosed. Manymodifications and variations will be apparent to those of ordinary skillin the art without departing from the scope and spirit of the invention.The embodiment was chosen and described in order to best explain theprinciples of one or more aspects of the invention and the practicalapplication, and to enable others of ordinary skill in the art tounderstand one or more aspects of the invention for various embodimentswith various modifications as are suited to the particular usecontemplated.

What is claimed is:
 1. A device comprising: an integrated circuit, theintegrated circuit comprising: a varying gate structure disposed over asubstrate structure, the varying gate structure comprising a first gatestack in a first region of the substrate structure, and a second gatestack in a second region of the substrate structure, wherein the firstgate stack is different from the second gate stack; a first field-effecttransistor in the first region of the substrate structure, the firstfield-effect transistor comprising the first gate stack of the varyinggate structure and having a first threshold voltage; and a secondfield-effect transistor in the second region of the substrate structure,the second field-effect transistor comprising the second gate stack ofthe varying gate structure and having a second threshold voltage,wherein the first threshold voltage is different from the secondthreshold voltage.
 2. The device of claim 1, wherein the varying gatestructure comprises one layer and another layer, the one layer having afirst thickness in the first region of the substrate structure and asecond thickness in the second region of the substrate structure, andthe another layer having a third thickness in the first region of thesubstrate structure and a fourth thickness in the second region of thesubstrate structure, wherein the first thickness is different from thesecond thickness, and the third thickness is different from the fourththickness.
 3. The device of claim 2, wherein the first thickness is lessthan the second thickness, and the third thickness is greater than thefourth thickness.
 4. The device of claim 1, wherein a portion of thevarying gate structure extends from the first field-effect transistor tothe second field-effect transistor.
 5. The device of claim 1, whereinthe first threshold voltage is between 80 and 120 millivolts greaterthan the second threshold voltage.
 6. The device of claim 1, wherein thesubstrate structure comprises a first fin extending over the firstregion of the substrate structure and a second fin extending over thesecond region of the substrate structure, and the varying gate structureis conformally disposed over the first fin and the second fin.
 7. Themethod of claim 6, wherein a portion of the varying gate structureextends from the first field-effect transistor to the secondfield-effect transistor.
 8. The device of claim 6, wherein the first finand the second fin are a common fin.
 9. The device of claim 1, whereinthe one layer of the varying gate structure comprises a work-functionlayer, and the another layer of the varying gate structure comprises acap layer, and the varying gate structure further comprises a gatedielectric layer disposed below the cap layer.
 10. A method comprising:fabricating an integrated circuit, the fabricating comprising: providinga varying gate structure disposed over a substrate structure, thevarying gate structure comprising a first gate stack in a first regionof the substrate structure and a second gate stack in a second region ofthe substrate structure, and the providing comprising: sizing one layerof the varying gate structure with a first thickness in the first regionof the substrate structure and a second thickness in the second regionof the substrate structure; and sizing another layer of the varying gatestructure with a third thickness in the first region of the substratestructure and a fourth thickness in the second region of the substratestructure, wherein the first thickness is different from the secondthickness, and the third thickness is different from the fourththickness.
 11. The method of claim 10, wherein the integrated circuitcomprises a first field-effect transistor in the first region of thesubstrate structure, and a second field-effect transistor in the secondregion of the substrate structure, the first field-effect transistorcomprising the first gate stack and having a first threshold voltage,and the second field-effect transistor comprising the second gate stackand having a second threshold voltage, wherein the first thresholdvoltage is different from the second threshold voltage.
 12. The methodof claim 11, wherein a portion of the varying gate structure extendsfrom the first field-effect transistor to the second field-effecttransistor.
 13. The method of claim 10, wherein the first thickness isless than the second thickness, and the third thickness is greater thanthe fourth thickness.
 14. The method of claim 10, wherein sizing the onelayer of the varying gate structure comprises: depositing, at leastpartially, a material of the one layer over the first region and thesecond region of the substrate structure; removing, at least partially,the material from the first region of the substrate structure; anddepositing again, at least partially, the material over the first regionand the second region of the substrate structure to form the firstthickness of the one layer in the first region, and the second thicknessof the one layer in the second region.
 15. The method of claim 10,wherein a third region of the substrate structure comprises a portion ofthe first region and another portion of the second region, and theproviding further comprises, after sizing the one layer of the varyinggate structure, resizing the one layer in the third region of thesubstrate structure with a fifth thickness.
 16. The method of claim 10,wherein the substrate structure comprises one or more fins extendingover the first region and the second region thereof, and providing thevarying gate structure comprises providing the varying gate structureconformally over the one or more fins.
 17. The method of claim 16,wherein the integrated circuit comprises a first field-effect transistorin the first region of the substrate structure and a second field-effecttransistor in the second region of the substrate structure, the firstfield-effect transistor comprising the first gate stack and a first finof the one or more fins, and having a first threshold voltage, and thesecond field-effect transistor comprising the second gate stack and asecond fin of the one or more fins, and having a second thresholdvoltage, wherein the first threshold voltage is different from thesecond threshold voltage.
 18. The method of claim 17, wherein a portionof the varying gate structure extends from the first field-effecttransistor to the second field-effect transistor.
 19. The method ofclaim 17, wherein the first fin and the second fin are a common fin ofthe one or more fin structures.
 20. The method of claim 10, wherein theone layer of the varying gate structure comprises a work-function layer,and the another layer of the varying gate structure comprises a caplayer, and the varying gate structure further comprises a gatedielectric layer disposed below the cap layer.